Click for original picture
Brand:aa
Product detail:
china good manufacture of stainless steel ball0.5mm-50.8mm(SGS approved )
Stainless steel balls have similar mechanical properties as chrome steel balls with the advantage of being resistant to corrosive environments. There are several types of stainless steel balls, ranging from the 440C type which offers the greatest hardness and surface finish to the 302 which has extreme toughness and corrosion resistance.
As one of the leading manufacturers of steel balls with 25 years' experience, we are in the position to supply steel balls with good quality and reasonable price.
Product Attribute:
Material: AISI304 AISI316 AISI420C AISI440C
Size: 0.8mm-150mm
Grade: G10 to G1000
Hardness: AISI304 and AISI316 are soft materials. For AISI420C after heat-treatment, the hardness is between HRC54-60. For AISI440C is HRC58-62
Certificate: IS9001:2008
Material Composition %
Material | C | Si | Mn | P | S | Ni | Cr | Mo |
AISI304 | 0.07 max | 1.0 max | 2.0 max | 0.045 max | 0.03 max | 8.0-10.5 | 17.0-19.0 | |
AISI316 | 0.07 max | 1.0 max | 2.0 max | 0.045 max | 0.03 max | 10.0-14.0 | 16.5-18.5 | 2.00-2.50 |
AISI420C | 0.40-0.50 | 1.0 max | 1.0 max | 0.04 max | 0.03 max | 1.0 max | 12.0-14.0 | |
AISI440C | 0.95-1.20 | 1.0 max | 1.0 max | 0.04 max | 0.03 max | 0.60 max | 16.0-18.0 | 0.40-0.80 |
Material AISI304, AISI316 and AISI420C can not make G10 balls.
Appications:
440C Stainless steel is a type of modern steel and famous for its high corrosion resistant, wear resistance, strength and hardness qualities among all the stainless alloys, capable of attaining (after heat treatment) the highest hardness (60 HRC). It has good resistance to the atmosphere, fresh water and mild acids. It has best resistance in the hardened, tempered and passivated condition. It allows creating a smooth polished surface and Razor sharp edges. It is being used in rolling element bearings, valve seats, casters, ball bearings and valve parts.
420C is a martensitic stainless steel with 12% Chromium which is sufficient to give good corrosive resistance properties. .It’s best corrosive resistance is when hardened and surface is ground or polished. It has good ductility in the annealed condition but can be hardened up to 500HB (highest of the chromium grades) due to its excellent harden-ability, it is capable of getting hardened up to 56 HRC Rockwell or higher. Martensitic Grades are known for high hardness and allowances must be made for poor weld ability and usually allowances for a final harden and temper treatment. 420 steel is magnetic and welding is not recommended. Material will not pass the 72 hours salt bath test.
316 is Austenitic stainless steel with features similar to AISI 302/304/304L series, but they can be anti-magnetic and, above all, the addition of molybdenum offers greater chemical resistance, particularly in sulfuric acid concentration. All balls can be annealed and passivated. The most common applications include their use in the chemical, paper and textile industries (valves, pumps and bearings).
Production process:
Drawing, Heading, Flashing, Heat-treatment, Grinding, Lapping1, Lapping2, Inspection, Packing.