Polypropylene Fiber for Engineering Construction
We have been exporting these fibres for many years, we are able to offer you the suitable fibre for your construction, we have more than 6 type fibre which be mixed with concrete for road making, construction, pls contact us for details if you have any interesting, thank you in advance.
Detailed Product Description
PP Fiber-Mesh
With polypropylene as raw material, this fiber appear net like structure with many fiber monofilaments connected.
PP Fiber-Mesh
With polypropylene as its raw material, this fiber appear net like structure with many fiber monofilaments connected.
When the fiber is put into the concrete, the horizontal structure in fiber monofilament can be destroyed in the course of stirring owing to friction and bubbing, and the fiber monofilament or net-like structure will fully stretch, thus the concrete is reinforced by a great number of polypropylene fibers.
As a new type concrete-strengthening fiber, it becomes a new popular subject in the fiber of fiber concrete research and application after glass and steel fiber
We have been exporting these fibre for more than ten years, we are able to offer you the suitable fibre for your construction, we have more than 6 type fibre which be mixed with concrete for road making, construction, pls contact us for details if you have any interesting, thank you in advance.
Fiber Item:
1.PP Fiber Monofilament
Raw Material | Polypropylene | Crack Elongation | 20%±5% |
Type | Monofilament | Density | 0.91±0.01 % g/cm3 |
Fiber Dia | 0.02-0.05±0.005mm | Melting Point | 160---170?/p> |
Tensile Strength | ≥450MPa | Resistance to Acid,Alkali | Strong |
Size | 6,10,12,15,19,20,24,48 | Water Absorbency | No |
2. PP Fiber Mesh
Density(g/cm3) | 0.91 | Elastic Modulas (MPa) | >3500 |
Length(mm) | 6,10,12,15,20 | Equivalent Diameter (m) | 100 |
Shape | Beam-like Net | Crack Elongation(%) | ≥10 |
Acid &Alkali Resistance | Strong | Water-Absorbency | No |
Tensile Strength(MPa) | 346-560 | Melting Point(C) | 160—170 |
3.PP Fiber Bunchy Twisted Form
Density(g/cm 3 ) | 0.91 | Elastic Modulus ( MPa) | >5000 |
Length(mm) | 54 | Equivalent Dia (mm) | 0.3+/- 0.05 |
Shape | bundle-like and twisted | Break tensile Ratio(%) | >15 |
Break Strength(MPa) | >560 | Resistance to acid, alkali | strong |
4.Curved PP Macro Fiber
Density(g/cm 3 ) | 0.91 | Elastic Modulas (MPa) | >5000 |
Length(mm) | 30,40,50 | Equivalent Dia(μm) | 80,100 |
Shape | curved bar | Break Tensile Ratio(%) | ≤155 |
Break Strength(MPa) | ≥460 | Melt Point | ≥160 |