RTV Silicone Rubber for Artificial Stone Molding

Brand:aa

Product detail:

Introduction of RTV Silicone Rubber for Artificial Stone Molding 

 

RTV Silicone Rubber for Artificial Stone Molding is a kind of two-component material, the silicone rubber consists of Part A base silicone and Part B CA30 curing agent, and Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction to become a silicone mold. These materials can be cast into the cured silicone molds to duplicating : plaster polyurethane, PU, GRC, cement, resin, polyester, wax etc...

 

Specifications of MC RTV-2 Silicone Rubber

 

Room Temperature Vulcanization

Equipped with REACH certificate

Professional technician with rich experience

4% catalyst offers for free of charge

Silicone hardness range: 10-60 shore A

High duplicating silicone molds

 

Features of RTV Silicone Rubber for Artificial Stone Molding 

 

1. Good flow ability and long working time

2. Medium hardness

3. High tear and tensile strength

4. Easy de-mould from complex replica parts

5. Acid and alkali-resistance

6. Low linear shrinkage

 

Applications of RTV Silicone Rubber for Artificial Stone Molding 

    

RTV2066/2088 silicone rubber are especially auitable for artificial stone mold making.

 

 

 

Instructions for Making Silicone Molds

 

1. Preparing

 

The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.

  

2. Mixing

 

Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100:2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35°C (95°F).it’s suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.

 

Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

  

3. Pouring and curing

 

Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

   

Storage of RTV Silicone Rubber for Artificial Stone Molding 

 

When the RTV Silicone Rubber is stored at or below 30 °C(85 °F) in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production. After 12 months,please use a stirring mill to stir the Part A silicone for some minutes, then the silicone rubber can be use again, no influence for other performance.

 

  

The information above is just for reference, if you're interested or have any questions, please feel free to contact Nicole: