Casting Stone Moldmaking RTV-2 Silicone

Brand:aa

Product detail:

Description of Casting Stone Moldmaking RTV-2 Silicone 

  

Decorative Stone Moldmaking RTV-2 Silicone is a kind of two-component material. The silicone is made up of Part A base silicone and Part B curing agent. The Part A base silicone and Part B CA curing agent can cure at room temperature by a condensation reaction, after full cure, it become a cured silicone mold. The silicone mold can be cast the following materials for reproduction: plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...

 

Characteristics of Casting Stone Moldmaking RTV-2 Silicone 

 

1. Good flow ability and long working time

2. Medium hardness

3. High tear and tensile strength

4. Easy de-mould from complex replica parts

5. Acid and alkali-resistance

6. Low linear shrinkage

 

Applications of Casting Stone Moldmaking RTV-2 Silicone 

 

RTV-2 Silicone series are suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. Etc.

 

RTV-2066 silicone is a kind of silicone which is especially suitable for the reproduction of artificial stone,cement stone,concrete stone and manufactured stone moldmaking.

 

Technical parameter of Casting Stone Moldmaking RTV-2 Silicone 

 

Item No.	RTV 2066
Color	off-white
Curing agent	CA30
Mixing ratio	100:2
Mixed viscosity	25000~26000 cps
Pot life	20-30 mins
Curing time	2-3 Hours
Hardness	28-30 Shore A
Tear Strength	27 N/mm
Tensile Strength	≥3.8 Mpa
Relative density	1.09~1.15 g/cm3
Shrinkage	≤0.3%
Elongation at break	420%
Methods of molding	Brushing/Pouring

 

 Storage of Casting Stone Moldmaking RTV-2 Silicone 

 

When the casting Stone Moldmaking RTV-2 Silicone is stored at or below 30 C (85F) in the original unopened containers, Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production.

 

 

FOQ of RTV-2 Silicone Rubber for Mold Making

 

 

Why does the RTV liquid silicone rubber for molding have few mold making times?

 

The silicone rubber mold has few molding times is due to follwoing reasons: adding too much silicone oil which will destroy the molecular of silicone rubber; making the mold for small and fine detailed products with higher hardness silicone rubber which is easy to break; making the mold for large products with soft silicone rubber which will reduce the tensile and tear strength of the mold, and the mold will have deformation. Thus, we should take the proper silicone rubber to make the mold for suitable products.

 

 

 

The information above is just for reference, if you're interested or have any questions, please feel free to contact Nicole:

Web:www(dot)mcsilicone(dot)com

E-mail:nicole(at)mcsilicone(dot)com

Skype:nicoleszmc

MSN: nicoleszmc (at)hotmail(dot)com