Shandong Liangshan Quanxing Plastic Co., Ltd. is founded in 1998 and located on the bank of the Yellow River which has a long history and also at the root of Liangshan Mountain which is famous both domestically and abroad. We enjoy beautiful mountains and clear water. It was founded in 1998 and specializes in producing various kinds of high quality and high technology black sheath materials for electric wires, cables and optical cables. Our representative products are black PE(LDPE,LLDPE,MDPE,HDPE) and PVC for cable and wire,also NHFR cable compound.   
  Shandong Liangshan Quanxing Plastic Co., Ltd. covers more than 10,000 square meters and has 160 staff members, of which 30% are professional technicians. The annual output of PE cable material is 10,000 tons. And PVC cable material is more than 11,000 tons since we have merged Henan Luoyang Quanxingsheng Cable Co., Ltd. in 2008. We also distribute pe general plastic materials more than 15,000 tons every year. 
Quanxing attained ISO9001 International Quality System Certification and SGS in 1999 and 2011. We have perfect inspection equipments which test all kinds of product parameters. Over years, through serving customers and orienting market by following the principle of "Reputation First, Quality Supremacy", we have won customers' trust and good comments by our good reputation and comprehensive services. There is no best but better in quality, no lowest but lower in price. We wholeheartedly welcome the visit and support from friends of various circles and sincerely invite partners of various fields to cooperate with us and create a beautiful future hand in hand.

                                 

Virgin plastics raw material hdpe for electrical cable and    wire insulation pellet

                                                 

No.	Property	Unit	Test	Data
1	Melt Flow Index	g/10min	GB/T3682-2000	≤2.0
2	Density	g/cm3	GB/T1033.1-2008	≤0.955-0.978
3	Tensile strength	Mpa	GB/T1040.3-2006	≥20.0
4	Tensile yied strength	Mpa	GB/T1040.3-2006	≥16
5	Elongation at break	%	GB/T1040.3-2006	≥650
6	Brittle temperature at low temperature	°C	GB/T5470-2008	≤-76
7	ESCR ,FO	H	GB/T2951.41-2008	≥500
8	Oxidation induction period at 200°C	Min	GB/T2951.42-2008	≥30
9	Content of Carbon black	%	GB/T2951.41-2008	2.60±0.25
10	Carbon Black dispersion	--	GB/T18251-2000	≤3
11	Ceka softening point	°C	GB/T1633-2000	110
12	Tensile strength after thermal aging	Mpa	GB/T2951.12-2008	≥20.0
12	Elongation after thermal aging	%	GB/T2951.12-2008	≥650
13	Elongation at Low Temperature	%	GB/T2951.14-2008	≥175
16	Dielectric strength	Mv/m	GB/T1408.1-2006	≥25
17	Volume resistivity	Ω.m	GB/T1410-2006	≥1*1014
18	Dielectric Constant ε	F/m	GB/T1409-2006	≤2.75
19	Dielectric loss factor tgδ	--	GB/T1409-2006	≤0.005