RTV-2 Liquid Silicone Molding Rubber

Brand:aa

Product detail:

Introduction of RTV-2 Liquid Silicone Molding Rubber 

 

RTV-2 silicone rubber is a kind of two-component material.The silicones rubber consist of Part A base silicones and Part B curing agent. When the two material are mixed together,the silicones base and curing agent can cure into a silicone mold by a condensation/addtion reflection in the room temperature.Then the silicones mold can be poured/brush on the following material for duplication:GRC,plaster,resin,cement,gympsum, polyurethane,PU,polyester etc.

  

Specifications of MC RTV-2 Silicone Rubber

 

Room Temperature Vulcanization

Equipped with REACH certificate

Professional technician with rich experience

4% catalyst offers for free of charge

Silicone hardness range: 10-60 shore A

High duplicating silicone molds

 

Applications of RTV-2 Liquid Silicone Molding Rubber 

 

RTV-2 silicone rubber can be applied in many objects mold making, since the RTV-2 silicone has good flow ability and medium hardness, and the silicone can cure at room temperature, thus it's a good material for duplication.

  

RTV-2 Silicone rubber can be used for artificial stone mold making. For example, RTV2030, RTV2066 and RTV2088 silicone.

 

RTV-2 Silicone rubber can be applied in candle and soap mold making, such as RTV215 and RTV218 silicone.

 

RTV-2 Silicone rubber can be used for plaster mold making, such as RTV2025, RTV2028 and RTV2030 silicone.

  

RTV-2 Silicone rubber can be applied in the field of shoe sole mold making, for example, RTV3010 and RTV3015 silicone.

  

RTV-2 Silicone rubber can be used for prototyping and electronic potting.

 

RTV-2 silicone rubber can be applied in the reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. Etc.

  

Datasheet of RTV-2 Liquid Silicone Molding Rubber 

  

Item	RTV 2024
Color	Liquid white
Curing agent	CA30
Mixing ratio	100:2
Mixed viscosity	20000-21000 cps
Working time	90-120 mins
Curing time	10-12 Hours
Hardness	24 Shore A
Tear Strength	35 N/mm
Tensile Strength	4.7 Mpa
Relative density	1.1-1.15 g/cm3
Elongation at break	544%

 

 

 

FOQ of RTV-2 Silicone Rubber for Mold Making

 

 

Why does the RTV liquid silicone rubber for molding have few mold making times?

 

The silicone rubber mold has few molding times is due to follwoing reasons: adding too much silicone oil which will destroy the molecular of silicone rubber; making the mold for small and fine detailed products with higher hardness silicone rubber which is easy to break; making the mold for large products with soft silicone rubber which will reduce the tensile and tear strength of the mold, and the mold will have deformation. Thus, we should take the proper silicone rubber to make the mold for suitable products.

 

 

 

The information above is just for reference, if you're interested or have any questions, please feel free to contact Nicole:

Web:www(dot)mcsilicone(dot)com

E-mail:nicole(at)mcsilicone(dot)com

Skype:nicoleszmc

MSN: nicoleszmc (at)hotmail(dot)com