2013 hot sales homopolymeric PVC by the suspension polymerization process for rigid extrusion of win

Brand:aa

Product detail:

2013 hot sales homopolymeric PVC by the suspension polymerization process for rigid extrusion of window or other profiles

 

 

PVC resin is the most widely raw material used in plastic production. It has good chemical stability corrosion resistance and water resistance. It can be dissolved in acetone , hydrochloric ether, ester and some alcohol . It can offer good solubility , good electrical insulation , thermoplasticity and membrane forming capacity.

The PVC Resins are polymerized by suspension process, their appearance being in white powder form.
They are essential materials for preparing PVC compounds. By adding blending agents and employing different techniques, they can be made into rigid or non-rigid PVC products and are suppliable in a wide range of transparent, translucent, and opaque colours.

 

Our PVC Resins are distinguished for their insulating, moisture-proof, oil-resistant, acid-resistant, and alkali-resitant properties.

Tape:	SG1	SG2	SG3	SG4	SG5	SG6	SG7	SG8
K value	77-75	74-73	72-71	70-69	68-66	65-63	62-60	59-55
Viscosity, ml/g	156-144	143-136	135-127	126-119	118-107	106-96	95-87	86-73
Average polymerization			1350-1250	1250-1150	1100-1000	950-850	950-850	750-650
Number of impurity particle max	30	30	30	30	30	30	40	40
Volatiles content % max	0.40	0.40	0.40	0.40	0.40	0.40	0.40	0.40
Appearing density g/ml min	0.42	0.42	0.42	0.42	0.42	0.45	0.45	0.45
Residual after sieve 0.25mm mesh max	2.0	2.0	2.0	2.0	2.0	2.0	2.0	2.0
0.063mm min	90	90	90	90	90	90	90	90
Number of grain/400cm2 max	40	40	40	40	40	40	40	40
Plasticizer absorbency value of 100g resin	25	25	25	22	19	16	14	14
Whiteness % min	74	74	74	74	74	74	70	70
Residual chlorethylenecontent mg/kg max	5	5	5	5	5	5	5	5
Ethylidene chloride mg/kg max	150	150	150	150	150	150	150	150