Sialon bonded silicon carbide brick  

 

 The producing peocess of refractory silicon carbide bricks

 

1) Silicon carbide refractory brick is made of sic raw material, mixed with SiO2 and C.

 

2) With all the material contact fully, the brick will be pressed under friction press, vibration molding, casting according to its shape.

 

3) After the billet making, it should be dried under room temperature for 2-3 days.

 

4)Then it will be sinstered in the high temperature furnace, pass through temperature rise period, temperature constant and temperature cooling period.

 

5) After sinstered, high quality bricks will be selected.

 

6) Seaworthy packing and timely delivery are supplied.

 

With different binding agents, they are devided into several types-for.

Tech Data and their applications are as follows:

 

1) Clay bonded silicon carbide refractory brick,

It is widely used in high temperature industry as refractory muffle board in industry kiln furnace, plate, sagger etc.

 

Item Brand	Apparent porosity(%)	Bulk density(g/cm3)	CCS(MPa)	Refractorness under load(T2,°C)	Thermal shock resistance(1100, °C,water-cooling)	SiC%
Standard value	≤20	≥2.5	≥80	≥1600	superior	≥85
Typical value	18	2.55	90	1650	superior	88

 

2) Oxide silicon carbide refractory,

It is used in ceramic industry.

 

Item Brand	Apparent porosity(%)	Bulk density(g/cm3)	CCS(MPa)	Hot bending strength Mpa(1400°C*1/2h,Mpa)	Thermal shock resistance(1100, °C,water-cooling)	SiC%
Standard value	≤19	≥2.55	≥80	≥15	superior	≥85
Typical value	18	2.6	110	16	superior	88

 

3) Nitride bonded silicon carbide refractory brick,

It is a kind of improvemental refractory products which is widely used in steel industry, smelting, metallurgy, aviation industry. It is also can be used as lining of blast furnace, lining of EAF(Electric arc furnace) or electric cells.

   

Item Brand	Apparent porosity(%)	Bulk density(g/cm3)	CCS(MPa)	CMOR(Mpa)	Thermal conductivity(w/m·k)	SiC%	Si3N4%
Standard value	≤18	≥2.65	≥120	≥30	≥15	≥72	≥18
Typical value	16	2.66	140	35	16	73	21

 

 

4) Sialon Bonded Silicon Carbide Bricks 

 

It is characterized by good resistance to oxidation and alkali corrosion, mainly used on the underside, belly and bosh of blast furnace.

 

Item		Si3N4 bonded Sic brick	Sialon bonded Sic brick
SiC, % ≥		72	70
Si3N4, % ≥		20	5(N)
Fe2O3, % ≤		0.7	0.7
Bulk density,g/cm3 ≥		2.65	2.65
Apparent porosity ≤		16	15
CCS, MPa ≥		150	150
Bending Strength, MPa MOR ≥	Room temp.	45	42
	High temp.1400×0.5hrs	45	50
Refractoriness under load(0.2MPa, 0.6%)≥		1700	1700
Thermal shock resistance,cycle(warter quenching at 1100°C)		30	30

 

 

 

 

The standard size of the bricks is 230*114*65mm. If you have other requirements about the shape, we can order as you need.

The tech data is just for preference. We can produce different levels as you require.

 

 

 

 

 