high grade ladle castables

Brand:aa

Product detail:

high grade ladle castables

 

Castable for steel ladle

Alumina-spinel castables(LQLC-90 and LQLC-85) mainly consist of fused white corundum, sintered tabular corundum and pure synthesized spinel.

The castables are highly resistant to slag corrosion and penetration when used as linings in continuous casting ladles.

High alumina-spinel (LQLC-80 and LQLC-90) are composed of sintered special grate bauxide and synthesied spinel from natural raw materials. The castables have strong resistance to corrosion, erosion and thermal shock. The service life of high alumina-magnesia castable LQLC -90 can be used for ladles within capacity of over 100tons, LQLC-80 for ladles with capactity between 50t to 90t and LQLC -75 for ladles below 50t.

 

physical and chemical properties:

 

Product name		LQLC-90	LQLC -85	LQLC -80	LQLC -75
chemical analysis %	AL2O3 Mgo	≥90 3~5	≥85 6~8	≥80 8~10	≥75 8~10
bulk density g/cm3	100°C×24h 1000°C×3h 1550°C×3h	≥3.15 ≥3.1 ≥3.0	≥3.0 ≥3.0 ≥2.95	≥2.90 ≥2.90 ≥2.80	≥2.85 ≥2.85 ≥2.80
permanent linear change %	100°C×24h 1000°C×3h 1550°C×3h	0~-0.1 -0.1~+0.1 0~+0.5	0~-0.1 -0.1~+0.1 0~+0.5	0~-0.1 -0.1~+0.1 0~+1.5	0~-0.1 -0.1~+0.1 0~+1.5
crushing strength Mpa	100°C×24h 1000°C×3h 1550°C×3h	≥35 ≥45 ≥85	≥30 ≥40 ≥80	≥45 ≥60 ≥60	≥40 ≥55 ≥55
bending strength Mpa	100°C×24h 1000°C×3h 1550°C×3h	≥5.0 ≥6.0 ≥8.0	≥4.0 ≥6.0 ≥8.0	≥7.0 ≥6.0 ≥9.0	≥6.0 ≥5.5 ≥8.0