High tensile Silicon Molybdenum Rod
1.MoSi2 heating element is a kind of resistance heating element made from Molybdenum Disilicide. It can be exerted under the high temperature of the oxidated atmosphere. MoSi2 elements have the unique function of high temperature anti-oxidation. Under the oxidated atmosphere, the maximum temperature of MoSi2 elements is 1800°C. It can be made into various types, including U-type, W-type, right-angle as well as circular type.
The general temperature of MoSi2 heating rods is from 1300°C to 1800°C, which is universally applied to the field of metallurgy, glass, ceramics, magnetic matrials, refractory materials, crystals, electron devices and kiln etc. It is the ideal heating element of high temperature anealing.
2.Technical Data
Density | Bending Strength | Hardness | Apparent Porosity | Water Absorption | Elongation | Fracture Toughness | Compressive Strength |
5.8g/cm3 | 350Mpa | 12.0Gpa | ±2% | 0 | 4% | 4.5Mpa.m1/2 | 650Mpa |
3.The influence of operation temperature on the heater surface in a different atmosphere
Atmosphere | 1700 Type | 1800 Type |
Air | 1700 | 1800 |
N2 | 1600 | 1700 |
He | 1600 | 1700 |
-80°C Dry H2 | 1150 | 1150 |
-20°C Wet H2 | 1450 | 1450 |
10%CO2, 50%CO, 15%H2 | 1600 | 1700 |
40%CO2, 20%CO | 1400 | 1450 |
Cracked and Partially Burnt Ammnia | 1400 | 1450 |
4. MoSi2 heating elements physics and chemistry characters:
1) Physics Characters
Volume Density | Bending Strength | Vickers Hardness | Porosity | Water absorption | Heating Elongation Rate |
5.5 g/cm3 | 15-25 kg/cm3 | (HV)570kg/mm2 | 7.4% | 1.2% | 4% |
2.)Chemistry Character
MoSi2 heating element is used in the high temperature under oxidizing atmosphere. It will form the SiO2 film which can keep the element from being melted. During the oxidizing process, the SiO2 protecting film is formed again when the element continues to be used. The MoSi2 heating element must not be used in the temperature between 400C and 700C for a long time, otherwise the element will be cremated under the strong oxidizing function in the low temperature.