E-Glass Multiaxial fiber glass fabric

Products Application

E-Glass multiaxial fiber glass fabric is made of e-glass direct roving parallel aligned in 0º, 90º, +45º, -45º, then stitched with or without a layer of chopped strand mat.

Each layer is typically oriented in one of four directions; Standard configurations offered by multiaxial fabric suppliers include biaxial(0º, 90º), double bias(+45º, -45º), triaxial warp(0º, +45º, -45º), triaxial weft(90º, +45º, -45º) and four axial (0º, 90º, +45º, -45º).

It’s compatible with UP, Vinyl Ester and Epoxy etc, used in GRP pultrusion process, hand lay-up process and RTM process etc, out-made products include GRP boats, automobile parts, wind energy blades etc.

Products Feature & Advantages

1. Mechanical property of different directions is adjustable.

2. The multi-layers structure could simplify forming process, improve operation efficiency.

3. Quickly wet-out, good molding property, easily to delete air bubbles.

Key Technical Data

Packing:

E-Glass Multiaxial fiber glass fabric is wound onto a paper tube which has an 

inside diameter of 90mm. The roll outside diameter is approximately 265mm. 

Each roll is wrapped up in plastic film and then packed in a cardboard box.  The 

rolls are stacked horizontally or vertically onto pallets. All pallets are stretch 

wrapped and strapped to maintain stability during transport.

Storage:

Unless otherwise specified,  powder chopped strand mats should be 

stored in a cool, dry, water-proof area. It is recommended that the room 

temperature and humidity be always maintained at 15c to 35c and 

35% to 65% respectively.