Pad Printing Silicone for pads making
Specifications Pad Printing Silicone for pads making
Pad printing silicon rubber features
1good printing effort
2clear printing
3without any impurity
4aging resistance
Technical Datesheets of pad printing silicone rubber :
Model | Appearance | Viscosity (cP) | Hardness (Shore A)
| Tensile strength (MPa) | Tear-strength (kN/m) | Elongation (%) | Mixing ratio ( %) | Pot life( min) | Curing time (h) |
901 | white | 32000±3000 | 21±2 | ≥3.0 | ≥15 | ≥350 | 2~3 | 30 | 2~4 |
902 | white | 28000±3000 | 28±2 | ≥3.2 | ≥18 | ≥400 | 2~3 | 30 | 2~4 |
912 | white | 28000±3000 | 29±2 | ≥3.5 | ≥18 | ≥380 | 2~3 | 30 | 2~4 |
916 | white | 28000±3000 | 14±2 | ≥3.2 | ≥20 | ≥420 | 2~3 | 30 | 2~4 |
Notes: Mixing ratio, Pot life and Demould time in above table is measured under room temperature of 25 °C, relative humidity of 65 to 70%.The datas is only for reference,. Mixing ratio should be modified according to various temperatures.
Performance:(check the information of RTV-2 introduction for reference)
Main application Pad Printing Silicone for pads making :
Pad printing silicone rubber is applicable to produce printing pads, mainly used for printing the irregular patterns on plactics toys, electroplating products, electronic toys, tradermarks ect.
This product is is featured as good printing effects, no particle,without any impurity, resistance the friction,and good resilience .And different colors ,like red, green, yellow, etc., are availabe according to the requirements of customers.
Packaging, storage and transportation
(1) The RTV-2 silicone rubber is packed with vacuumed thick PE bag inside,and iron barrel (tin) outside, packing in 5 kg, 20 kg , 200 kg.
Curing agent (catalyst, cross-linking agent or other additives) are packed with 1 kg, 25 kg plastic bottles or barrels, and the weight is 3-5% of total silicone.
(2) The product should be stored in a cool dry place, avoid the sun and rain, it must be kept away from acids, alkalis, salts and other compounds. The shelf life is one year from the date of production.For some models, after three months, the viscosity will increase, which will be, generally speaking, no effect to its performance. It can be re-used through a re-examination even If over its storage period. Curing agent is easy to absorb moisture and get volatilized, so the deterioration should be sealed for storage.
(3) The goods is NOT subject to IMDG except the curing agent.