Item

Test conditions

Test method

Test data

unit

Density 

ISO 1183:1987

1040

kg/m3

Water absorption

ISO 62:1999

<0.1

%

Melt flow rate

200°C/5kg

ISO 1133:1997

3.8

cm3/10min

Process shrinkage

ISO 294-4:1997

0.4-0.6

%

Charpy impact strength 

1eU

ISO 179:1993

15

kj/m2

Tensile modulus

1mm/min

ISO 527-2:1993

3300

MPa

Elongation 

50mm/min

ISO 527-2:1993

3

%

Tensile strength at break

50mm/min

ISO 527-2:1993

55

MPa

Ball indentation hardness H

358N/30s

ISO 2039-1:1993

150

N/mm2

Bending strength

2mm/min

ISO 178:1993

100

MPa

HDT

1.8MPa

ISO 75-2:1993

84

°C

Linear coefficient of thermal expansion

(23-80)°C

DIN 53 752

0.8-1.0

K-1

Heat conduction

DIN 52 612

0.16

W/mK

Vicat softening point

B50/oil

ISO 306:1994

93

°C

Flame retardance

>1.4mm

UL-Standard 94

94HB

Class