Click to enlarge
Flame Retardant:C- Self Extinguishing Grade
Regular Grade:
A Standard Grade
B High Expansion Grade
D Fast Cycling Grade
Properties
eps Main Component: 92%~96% polystyrene
Appearance: Colorlessly transparent or opaque tiny beads
Density: about 1.04
Bulk density: about 0.6
Item | Test conditions | Test method | Test data | unit |
Density |
| ISO 1183:1987 | 1040 | kg/m3 |
Water absorption |
| ISO 62:1999 | <0.1 | % |
Melt flow rate | 200°C/5kg | ISO 1133:1997 | 3.8 | cm3/10min |
Process shrinkage |
| ISO 294-4:1997 | 0.4-0.6 | % |
Charpy impact strength | 1eU | ISO 179:1993 | 15 | kj/m2 |
Tensile modulus | 1mm/min | ISO 527-2:1993 | 3300 | MPa |
Elongation | 50mm/min | ISO 527-2:1993 | 3 | % |
Tensile strength at break | 50mm/min | ISO 527-2:1993 | 55 | MPa |
Ball indentation hardness H | 358N/30s | ISO 2039-1:1993 | 150 | N/mm2 |
Bending strength | 2mm/min | ISO 178:1993 | 100 | MPa |
HDT | 1.8MPa | ISO 75-2:1993 | 84 | °C |
Linear coefficient of thermal expansion | (23-80)°C | DIN 53 752 | 0.8-1.0 | K-1 |
Heat conduction |
| DIN 52 612 | 0.16 | W/mK |
Vicat softening point | B50/oil | ISO 306:1994 | 93 | °C |
Flame retardance | >1.4mm | UL-Standard 94 | 94HB | Class |