GR5 titanium alloy bar
Ti-6Al-4V is a two phase alpha + beta grade of titanium and is the most widely used of all the titanium grades. It is supplied in the annealed condition as per the AMS 4928R or BS2TA11for ease of machinability and can be strengthened with a relatively simple heat treatment to offer very high mechanical properties.
The combination of these good mechanical properties (maintained up to ~400oC), a low density of 4.42 g/cm3 and a very good corrosion resistance make the Ti-6Al-4V ideal for applications in the aerospace, marine, offshore oil & gas and motorsport industries.
GR5 titanium alloy bar Applications :
Offshore & Marine
Offshore tubulars and oil and gas equipment.
Aerospace
Compressor blades, discs and rings for jet engines, airframe components, fasteners, rocket engine cases, helicopter rotor hubs and critical forgings.
Other
Biomedical implants, and chemical processing equipment.
Nominal Composition
Ti Rem, Al 6%, V 4%, Fe 0.3% max
Key Features
1.Very High Strengh Capabilities
2.Good Corrosion Resistance
3.Excellent strength to weight ratio
4.High Strength at cryogenic temperatures.
5.Good Weldability
specifications:
ASTM F67 Medical titanium bar
1) Chemical composition(WT% Max)
Grade | N | C | H | Fe | O | Ti |
Grade 1 | 0.03 | 0.08 | 0.015 | 0.20 | 0.18. | balanced |
Grade 2 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | balanced |
Grade 3 | 0.05 | 0.08 | 0.015 | 0.30 | 0.35 | balanced |
Grade 4 | 0.05 | 0.08 | 0.015 | 0.50 | 0.40 | balanced |
2) Properties
Grade | Tesile strength(Min) Ksi Mpa | Yield strength 0.2%(Min) Ksi Mpa | Elongation (Min) % | Reduction of Area (Min) % | ||
Grade 1 | 35 | 240 | 25 | 170 | 24 | 30 |
Grade 2 | 50 | 345 | 40 | 275 | 20 | 30 |
Grade 3 | 65 | 450 | 55 | 380 | 18 | 30 |
Grade 4 | 80 | 550 | 70 | 483 | 15 | 25 |
Gr5 ELI ASTM F136 Medical titanium bar
Chemical composition(WT% Max)
N | C | H | Fe | O | Al | V | Each | Total | Ti |
0.05 | 0.08 | 0.012 | 0.25 | 0.13 | 5.5-6.75 | 3.5-4.5 | 0.1 | 0.4 | balanced |